Feeder Element for Metal Casting

ABSTRACT

The present invention discloses a feeder element for use in metal casting, said feeder element comprising: (i) a first end for mounting on a mould pattern; (ii) an opposite second end for receiving a feeder sleeve,—and (iii) a bore between—the first and second ends defined by a stepped sidewall; said feeder element being compressible in use whereby to reduce the distance between the first and second ends, wherein the stepped sidewall has a first sidewall region defining the second end of the element and a mounting surface ( 54 ) for a feeder sleeve in use, said first sidewall region being inclined to the bore axis by less than 90° and a second sidewall region contiguous with the first sidewall region, said second sidewall region being parallel to or inclined to the bore axis at a different angle to the first sidewall region whereby to define a step in the sidewall. The feeder element offers improvements over the element disclosed in WO2005/051568.

The present invention relates to an improved feeder element for use in metal casting operations utilising casting moulds, especially but not exclusively in medium-pressure sand moulding systems.

In a typical casting process, molten metal is poured into a pre-formed mould cavity which defines the shape of the casting. However, as the metal solidifies it shrinks, resulting in shrinkage cavities which in tmm result in unacceptable imperfections in the final casting. This is a well known problem in the casting industry and is addressed by the use of feeder sleeves or risers which are integrated into the mould during mould formation. Each feeder sleeve provides an additional (usually enclosed) volume or cavity which is in communication with the mould cavity, so that molten metal also enters into the feeder sleeve. During solidification, molten metal within the feeder sleeve flows back into the mould cavity to compensate for the shrinkage of the casting. It is important that metal in the feeder sleeve cavity remains molten longer than the metal in the mould cavity, so feeder sleeves are made to be highly insulating or more usually exothermic, so that upon contact with the molten metal additional heat is generated to delay solidification.

After solidification and removal of the mould material, unwanted residual metal from within the feeder sleeve cavity remains attached to the casting and must be removed. In order to facilitate removal of the residual metal, the feeder sleeve cavity may be tapered towards its base (i.e. the end of the feeder sleeve which will be closest to the mould cavity) in a design commonly referred to as a neck down sleeve. When a sharp blow is applied to the residual metal it separates at the weakest point which will be near to the mould (the process commonly known as “knock off”). A small footprint on the casting is also desirable to allow the positioning of feeder sleeves in areas of the casting where access may be restricted by adjacent features.

Although feeder sleeves may be applied directly onto the surface of the mould cavity, they are often used in conjunction with a breaker core. A breaker core is simply a disc of refractory material (typically a resin bonded sand core or a ceramic core or a core of feeder sleeve material) with a hole in its centre which sits between the mould cavity and the feeder sleeve. The diameter of the hole through the breaker core is designed to be smaller than the diameter of the interior cavity of the feeder sleeve (which need not necessarily be tapered) so that knock off occurs at the breaker core close to the mould.

Breaker cores may also be manufactured out of metal. DE 196 42 838 A1 discloses a modified feeding system in which the traditional ceramic breaker core is replaced by a rigid flat annulus and DE 201 12 425 U1 discloses a modified feeding system utilising a rigid “hat-shaped” annulus.

Casting moulds are commonly formed using a moulding pattern which defines the mould cavity. Pins are provided on the pattern plate at predetermined locations as mounting points for the feeder sleeves. Once the required sleeves are mounted on the pattern plate, the mould is formed by pouring moulding sand onto the pattern plate and around the feeder sleeves until the feeder sleeves are covered and the mould box is filled. The mould must have sufficient strength to resist erosion during the pouring of molten metal, to withstand the ferrostatic pressure exerted on the mould when full and to resist the expansion/compression forces when the metal solidifies.

Moulding sand can be classified into two main categories. Chemical bonded (based on either organic or inorganic binders) or clay-bonded. Chemically bonded moulding binders are typically self-hardening systems where a binder and a chemical hardener are mixed with the sand and the binder and hardener start to react immediately, but sufficiently slowly enough to allow the sand to be shaped around the pattern plate and then allowed to harden enough for removal and casting.

Clay-bonded moulding uses clay and water as the binder and can be used in the “green” or undried state and is commonly referred to as greensand. Greensand mixtures do not flow readily or move easily under compression forces alone and therefore to compact the greensand around the pattern and give the mould sufficient strength properties as detailed previously, a variety of combinations of jolting, vibrating, squeezing and ramming are applied to produce uniform strength moulds at high productivity. The sand is typically compressed (compacted) at high pressure, usually using a hydraulic ram (the process being referred to as “ramming up”). With increasing casting complexity and productivity requirements, there is a need for more dimensionally stable moulds and the tendency is towards higher ramming pressures which can result in breakage of the feeder sleeve and/or breaker core when present, especially if the breaker core or the feeder sleeve is in direct contact with the pattern plate prior to ram up.

The above problem is partly alleviated by the use of spring pins. The feeder sleeve and optional locator core (similar in composition and overall dimensions to breaker cores) is initially spaced from the pattern plate and moves towards the pattern plate on ram up. The spring pin and feeder sleeve may be designed such that after ramming, the final position of the sleeve is such that it is not in direct contact with the pattern plate and may be typically 5 to 25 mm distant from the pattern surface. The knock off point is often unpredictable because it is dependent upon the dimensions and profile of the base of the spring pins and therefore results in additional cleaning costs. The solution offered in EP-A-1184104 is a two-part feeder sleeve. Under compression during mould formation, one mould (sleeve) part telescopes into the other. One of the mould (sleeve) parts is always in contact with the pattern plate and there is no requirement for a spring pin. However, there are problems associated with the telescoping arrangement of EP-A-1184104. For example, due to the telescoping action, the volume of the feeder sleeve after moulding is variable and dependent on a range of factors including moulding machine pressure, casting geometry and sand properties. This unpredictability can have a detrimental effect on feed performance. In addition, the arrangement is not ideally suited where exothermic sleeves are required. When exothermic sleeves are used, direct contact of exothermic material with the casting surface is undesirable and can result in poor surface finish, localised contamination of the casting surface and even sub-surface gas defects.

Yet a further disadvantage of the telescoping arrangement of EP-A-1184104 arises from the tabs or flanges which are required to maintain the initial spacing of the two mould (sleeve) parts. During moulding, these small tabs break off (thereby permitting the telescoping action to take place) and simply fall into the moulding sand. Over a period of time, these pieces will build up in the moulding sand. The problem is particularly acute when the pieces are made from exothermic material. Moisture from the sand can potentially react with the exothermic material (e.g. metallic aluminium) creating the potential for small explosive defects.

An attempt to mitigate the effect of sleeve breakage is made in DE 201 12 425 U1 by providing the mounting surface that bears the weight of the sleeve with a pair of spaced apart lips that with the mounting surface form a channel or groove within which the sleeve sits. The inner lip prevents broken pieces of the sleeve falling into the mould and the outer lip prevents broken pieces from falling into the moulding sand.

WO2005/051568 (the entire disclosure of which is incorporated herein by reference) discloses a feeder element (a collapsible breaker core) that is especially useful in high-pressure sand moulding systems. The feeder element has a first end for mounting on a mould pattern, an opposite second end for receiving a feeder sleeve and a bore between the first and second ends defined by a stepped sidewall. The stepped sidewall is designed to deform irreversibly under a predetermined load (corresponding to the crush strength). The feeder element offers numerous advantages over traditional breaker cores including:—

(i) a smaller feeder element contact area (aperture to the casting); (ii) a small footprint (external profile contact) on the casting surface; (iii) reduced likelihood of feeder sleeve breakage under high pressures during mould formation; and (iv) consistent knock off with significantly reduced cleaning requirements.

The feeder element of WO2005/051568 is exemplified in a high-pressure sand moulding system. The high ramming pressures involved necessitate the use of high strength (and high cost) feeder sleeves. This high strength is achieved by a combination of the design of the feeder sleeve (i.e. shape, thickness etc.) and the material (i.e. refractory materials, binder type and addition, manufacturing process etc.). The examples demonstrate the use of the feeder element with a FEEDEX HD-VS159 feeder sleeve, which is designed to be pressure resistant (i.e. high strength) and for spot feeding (high density, highly exothermic, thick walled, not high volume feed demand). The feeder sleeve is secured to the feeder element via a mounting surface which bears the weight of the feeder sleeve and which is perpendicular to the bore axis. For medium pressure moulding there is the potential opportunity of using lower strength sleeves i.e. different designs (shapes and wall thicknesses etc.) and/or different composition (i.e. lower strength). Irrespective of the sleeve design and composition, in use there would still be the issues associated with knock off from the casting (variability and size of footprint on the casting) and need for good sand compaction beneath the feeder element. If the feeder element of WO20051051568 were to be employed in medium-pressure moulding lines it would be necessary to design the element so that it collapses sufficiently at the lower moulding pressure (as compared to high pressure moulding) i.e. to have a lower initial crush strength. It would also be highly advantageous to use lower strength feeder sleeves (typically lower density sleeves), which would allow for a greater range of sleeve designs and compositions to be used successfully and optimally for a greater range of casting types and correspondingly lower cost feeder sleeves. However, when this was attempted the inventors surprisingly discovered that the feeder sleeve suffered damage and breakages on moulding which if used for casting would have resulted in the casting suffering from defects.

It is an object of the present invention in a first aspect to provide an improved feeder element which can be used in a cast moulding operation. In particular, it is an object of the present invention in its first aspect to extend the utility of collapsible feeder elements into medium pressure moulding systems while allowing the use of relatively weak feeder sleeves without introducing casting defects.

According to a first aspect of the present invention, there is provided a feeder element for use in metal casting, said feeder element comprising:

(i) a first end for mounting on a mould pattern; (ii) an opposite second end for receiving a feeder sleeve; and (iii) a bore between the first and second ends defined by a stepped sidewall; said feeder element being compressible in use whereby to reduce the distance between the first and second ends, wherein the stepped sidewall has a first sidewall region defining the second end of the element and a mounting surface for a feeder sleeve in use, said first sidewall region being inclined to the bore axis by less than 90° and a second sidewall region contiguous with the first sidewall region, said second sidewall region being parallel to or inclined to the bore axis at a different angle to the first sidewall region whereby to define a step in the sidewall.

The feeder element may comprise additional sidewall regions, whereby multiple steps in the sidewall are defined, in which case at least one of the additional sidewall regions is preferably inclined at a greater angle to the axis than the first sidewall region.

It will be noted upon reading WO2005/051568 that, although the orientation of the sidewall region defining the mounting surface for the feeder sleeve and bearing the weight of the feeder sleeve is not particularly limited, it is said to be preferably perpendicular to the bore axis as is shown in all of the examples. The only significance placed on the orientation of this surface is that the perpendicular arrangement is the most convenient for mounting the sleeve.

Preferably the first sidewall region is inclined to the bore axis at an angle of between 50 and 85°, more preferably at an angle of between 15° and 80°, even more preferably at an angle of between 25° and 75°, and most preferably at an angle of between 30° and 70°. For example, the first sidewall region may be inclined to the bore axis at an angle of 60°.

It will be understood that the amount of compression and the force required to induce compression will be influenced by a number of factors including the material of manufacture of the feeder element and the shape and thickness of the sidewall. It will be equally understood that individual feeder elements will be designed according to the intended application, the anticipated pressures involved and the feeder size requirements.

Preferably, the initial crush strength (i.e. the force required to initiate compression and irreversibly deform the feeder element over and above the natural flexibility that it has in its unused and uncrushed state) is no more than 5000 N, and more preferably no more than 3000 N. If the initial crush strength is too high, then moulding pressure may cause the feeder sleeve to fail before compression is initiated. Preferably, the initial crush strength is at least 250 N. If the crush strength is too low, then compression of the element may be initiated accidentally, for example if a plurality of elements is stacked for storage or during transport.

The feeder element of the present invention may be regarded as a collapsible breaker core as this term suitably describes some of the functions of the element in use. Traditionally, breaker cores comprise resin bonded sand or are a ceramic material or a core of feeder sleeve material. However, the feeder element of the current invention can be manufactured from a variety of other suitable materials including metal. In certain configurations it may be more appropriate to consider the feeder element to be a feeder neck.

As used herein, the term “compressible” is used in its broadest sense and is intended only to convey that the length of the feeder element between its first and second ends is shorter after compression than before compression. Preferably, said compression is non-reversible i.e. after removal of the compression inducing force the feeder element does not revert to its original shape.

In a particularly preferred embodiment, the stepped sidewall of the feeder element comprises a first series of sidewall regions (said series having at least one member) in the form of rings (which are not necessarily planar) of increasing diameter (when said series has more than one member) interconnected and integrally formed with a second series of sidewall regions (said second series having at least one member). Preferably, the sidewall regions are of substantially uniform thickness, so that the diameter of the bore of the feeder element increases from the first end to the second end of the feeder element. Conveniently, the second series of sidewall regions are cylindrical (i.e. parallel to the bore axis), although they may be frustoconical (i.e. inclined to the bore axis). Both series of sidewall regions may be of non-circular shape (e.g. oval, square, rectangular, or star shaped). The second sidewall region constitutes the sidewall region of the second series closest to the second end of the feeder element.

The compression behaviour of the feeder element can be altered by adjusting the dimensions of each sidewall region. In one embodiment, all of the first series of sidewall regions have the same length and all of the second series of sidewall regions have the same length (which may be the same as or different from the first series of sidewall regions and which may be the same as or different from the first sidewall region). In a preferred embodiment however, the length of the first series of sidewall regions and/or the second series of sidewall regions incrementally increases towards the first end of the feeder element.

The feeder element may be defined by the first sidewall region and one each of the first and second series of sidewall regions. However, the feeder element may have as many as six or more of each of the first and the second series of sidewall regions. In a particularly preferred embodiment, four of the first series and five of the second series are provided.

Preferably, the thickness of the sidewall regions is from about 4 to 24%, preferably from about 6 to 20%, more preferably from about 8 to 16% of the distance between the inner and outer diameters of the first sidewall regions (i.e. the annular thickness in the case of planar rings (annuli)).

Preferably, the distance between the inner and outer diameters of the first series of sidewall regions is 4 to 10 ml and most preferably 5 to 7.5 mm. Preferably, the thickness of the sidewall regions is 0.2 to 1.5 mm and most preferably 0.3 to 1.2 mm. The ideal thickness of the sidewall regions will vary from element to element and be influenced by the size, shape and material of the feeder element, and by the process used for its manufacture.

In a convenient embodiment, only an edge contact is formed between the feeder element and casting, the first end (base) of the feeder element being defined by a sidewall region of the first or second series which is non-perpendicular to the bore axis. It will be appreciated from the foregoing discussion that such an arrangement is advantageous in minimising the footprint and contact area of the feeder element. In such embodiments, the sidewall region which defines the first end of the feeder element may have a different length and/or orientation to the other sidewall regions of that series. For example, the sidewall region defining the base may be inclined to the bore axis at an angle of 5 to 30°, preferably 5 to 15°. Preferably, the free edge of the sidewall region defining the first end of the feeder element has an inwardly directed annular flange or bead.

It will be understood from the foregoing discussion that the feeder element is intended to be used in conjunction with a feeder sleeve. Thus, the invention provides in a second aspect a feeder system for metal casting comprising a feeder element in accordance with the first aspect and a feeder sleeve secured thereto.

A standard feeder sleeve has an annular base for mounting onto a breaker core (collapsible or otherwise). In the feeder system of the second aspect the base of the feeder sleeve is profiled at the same angle as the first sidewall region of the feeder element.

The nature of the feeder sleeve is not particularly limited and it may be for example insulating, exothermic or a combination of both. Neither is its mode of manufacture particularly limited, it may be manufactured for example using either the slurry or core-shot method. Typically a feeder sleeve is made from a mixture of refractory fillers (e.g. fibres, hollow microspheres and/or particulate materials) and binders. An exothermic sleeve further requires a fuel (usually aluminium or aluminium alloy) and usually initiators/sensitisers. Suitable feeder sleeves include for example those sold by Foseco under the trade name KALMIN, KALMINEX or FEEDEX. Feeder sleeves are available in a number of shapes including closed and open cylinders, ovals, neckdowns and domes. Preferably the feeder element is used in conjunction with any conventional insert sleeve design which consists of a closed (capped) sleeve that may be flat topped, domed, flat topped dome, or any other insert sleeve design. The feeder sleeve may be conveniently secured to the feeder element by adhesive but may also be push fit or have the sleeve moulded around part of the feeder element. Preferably the feeder sleeve is adhered to the feeder element.

The invention allows the use of lower strength sleeves to be used down to a value of 3.5 kN. Preferably, the sleeve strength is at least 5 kN. Preferably, the sleeve strength is less than 20 kN. For ease of comparison the strength of a feeder sleeve is defined as the compressive strength of a 50×50 mm cylindrical test body made from the feeder sleeve material. A 201/70 EM compressive testing machine (Form & Test Seidner, Germany) is used and operated in accordance with the manufacturer's instructions. The test body is placed centrally on the lower of the steel plates and loaded to destruction as the lower plate is moved towards the upper plate at a rate of 20 mm/minute. The effective strength of the feeder sleeve will not only be dependent upon the exact composition, binder used and manufacturing method, but also on the size and design of the sleeve, which is illustrated by the fact that the strength of a test body is usually higher than that measured for a standard flat topped 6/9K sleeve. The potential availability of a greater range of sleeve compositions and designs that can be used together with the invention enables the most appropriate (technically and economically) sleeve to be specified for each individual casting, which is not possible with the existing prior art.

Embodiments of the invention will now be described by way of example only with reference to the accompanying drawings in which:—

FIG. 1 is a cross section of a test piece containing features of the feeder element in accordance with invention.

FIGS. 2 a and 2 b are a cross section and a top view respectively of a known feeder element.

FIG. 3 a is a known VSK feeder sleeve design.

FIG. 3 b is a known 6/9K feeder sleeve design.

FIG. 3 c is a flat topped dome feeder sleeve design.

FIG. 4 is a cross section of another known feeder element.

FIGS. 5 a to 5 c are computer simulations of the known feeder element of FIG. 4 in use.

FIG. 6 is a cross section of a feeder element in accordance with the invention.

FIGS. 7 a and 7 b are computer simulations of the feeder element of FIG. 6 in use.

FIG. 8 is a cross section of another feeder element in accordance with the invention.

FIG. 9 is a flat topped dome feeder sleeve with modified base together with a feeder element in accordance with the invention.

FIG. 10 a is a plot of force applied against displacement for a KALMINEX 2000ZP 6/9K feeder sleeve under compression

FIGS. 10 b to 10 i are plots of force applied against displacement for the test pieces of FIG. 1 together with a KALMINEX 2000ZP 6/9K feeder sleeve with varying angle α.

METHODOLOGY

In the subsequent examples standard feeder systems comprising standard feeder elements with standard feeder sleeves were tested as well as feeder systems in accordance with the present invention. Both the standard and inventive feeder elements are manufactured by pressing sheet steel. The profiling of the base of the inventive feeder sleeves was achieved either by manufacturing the sleeves with the profile already in place (flat topped dome shaped sleeves) or by the use of abrasive paper on standard sleeves (6/9K shaped sleeves). When manufacturing the profiled 6/9K shaped feeder sleeves commercially it will be understood that it would be more practical to produce the feeder sleeves with the profile already in place.

Moulding Test

Testing was conducted on a commercial Herman moulding machine using a clay-bonded greensand system. A wooden pattern plate was bolted to a steel plate. Four feeder elements and corresponding feeder sleeves were then mounted onto the pattern plate using locating pins, spaced 150 mm and 114 mm from the centre lines of the pattern plate. A moulding flask was placed on the pattern plate to give a mould of approximate dimensions 576 mm×432 mm×192 mm (length×width×height). Sand was added to the flask such that its level was approximately 50 mm above the height of the flask. The weight of sand was approximately 112 kg. A 576×432 mm ram plate was positioned 144 mm above the height of the flask (approximately 94 mm above the surface of the non-compressed sand) and the mould compressed by downward movement of the ram plate to the prescribed pressure, taking between 3 and 6 seconds to compact the sand to the level of the moulding flask. The mould was then excavated and the condition of the feeder elements and feeder sleeves was observed.

Compression Test

Feeder element test pieces and feeder sleeves were tested by sitting them between the two parallel plates of a Hounsfield compression strength tester.

The bottom plate was fixed, whereas the top plate traversed downwards via a mechanical screw thread mechanism at a constant rate of 30 mm per minute and graphs of force applied against plate displacement were plotted.

The feeding element test pieces that were compression tested had the basic configuration shown in FIG. 1. Briefly, the feeder element test piece 10 consists of a circular base 12 (of diameter D) with a cylindrical sidewall region 14 (of height h) extending upwardly therefrom. Contiguous with the cylindrical sidewall region 14 is an outwardly tapering sidewall region 16 (with a maximum diameter d) which is inclined toward the cylindrical sidewall region 14 by an angle α. The tapering sidewall region 16 serves as a mounting surface for a feeder sleeve in use. It will be noted that these test pieces used for compression testing are not provided with an opening in the base since they will not be used for casting.

Various feeder elements were prepared where α=90° (standard), 80°, 70°, 60°, 50°, 40°, 30° or 20°. The test pieces were manufactured from mild steel with a thickness of 0.5 mm. In the case of the standard feeder element test piece (α=90°) D was 53.5 mm, h was 7.5 mm and d was 80.0 mm. The test pieces were designed such that the height (h) of the cylindrical sidewall region 14, the maximum diameter (d) of the outwardly tapering sidewall region 16 and the area of the mounting surface provided by the first sidewall region 16 remained constant whilst a was varied (i.e. as a decreases, the diameter (D) of the circular base 12 increases). The feeder elements were tested with a KALMINEX 2000ZP 6/9K exothermic feeder sleeve as supplied by Foseco having a density of 0.55-0.65 g/cm² and a compression strength of the order 4 kN.

COMPARATIVE EXAMPLE 1 Moulding Test

A feeder element (a metal collapsible breaker core sold under the nomenclature MH/33 as described in WO2005/051568 and shown in FIGS. 2 a and 2 b) was tested in combination with the following feeder sleeves listed in Table 1:

TABLE 1 FEEDEX KALMINEX KALMINEX KALMINEX HD 95 2000XP 2000XP Shape VSK (thick 6/9K (parallel 6/9K (parallel Flat topped walled mini- conical capped conical capped dome (flat- sleeve as insert sleeve insert sleeve topped closed shown in with Williams with Williams dome sleeve FIG. 3a) wedge as wedge as with variable shown in shown in wall section as FIG. 3b) FIG. 3b) shown in FIG. 3c) Manufacturing Core shot Slurry formed Core shot Core shot Process Density (gcm⁻³) 1.35-1.45 0.85-0.95 0.55-0.65 0.55-0.65 Strength (kN)^(a) High (>25) Medium (10-11) Medium (11-12) Medium (11-12) Strength (kN)^(b) n/a Medium (8-9) Medium (9-10) n/a ^(a)strength of standard cylindrical test body ^(b)strength of actual 6/9K sleeve

The sleeve formulations vary according to the required product properties, however, all have the general formulation: 20-25% aluminium fuel; 10-20% oxidants and sensitisers; 5-10% organic binders; and 35-55% refractory fillers. The type of refractory fillers used has the most direct influence on both density and strength of the sleeves.

Referring to FIGS. 2 a and 2 b, the feeder element 20 comprises a first end (base) 22 for mounting on a mould pattern; an opposite second end (top) 24 for receiving a feeder sleeve; and a bore 26 between the first and second ends 22, 24 defined by a stepped sidewall 28. The second end 24 of the feeder element 20 is defined by a first sidewall region 25, said first sidewall region 25 being perpendicular to the bore axis A. A second sidewall region 30 is contiguous with the first sidewall region 25 and parallel to the bore axis A. The stepped sidewall 28 additionally comprises an alternating series of first 28 a and second 28 b sidewall regions of approximately equal length. The second sidewall region 30 constitutes the first sidewall region of the second series 28 b closest to the second end 24 of the feeder element 20. The first series of sidewall regions 28 a consists of three sidewall regions that are perpendicular to the bore axis A. The second series of sidewall regions 28 b consists of four sidewall regions. The first three sidewall regions of the second series 28 b are parallel to the bore axis A. The fourth sidewall region 32 is inclined to the bore axis A at an angle of 15° and has an inwardly directed annular flange in order to minimise its footprint and thus improve knock off. The fourth sidewall region 32 is also approximately twice the length of the other sidewalls of the second series 28 b.

The feeder elements and feeder sleeves were moulded as described above using a moulding pressure of 380 PSI (2620 kN). The feeder elements collapsed as expected and there was no visible damage to the FEEDEX HD VSK feeder sleeve, however, there was cracking and some breakages at the base of the KALMINEX 95 6/9K sleeve and KALMINEX 2000XP dome sleeve as well as some slumping (compression of the sleeve). The KALMINEX 2000XP 6/9K sleeve showed severe damage and the sleeve base was broken into several pieces. A KALMINEX 2000ZP feeder sleeve was not tested with the feeder element 20 because it is weaker than the KALMINEX XP and KALMINEX 95 feeder sleeves which suffered from damage at 380 PSI (2620 kN).

The series of tests were then repeated at the higher moulding pressure of 620 PSI (4275 kN). Again, all of the feeder elements collapsed, however this time there was visible damage to all of the sleeves. At the base of the FEEDEX HD VSK sleeve there were some small internal cracks and in one instance a chip close to the feeder element. For the KALMINEX 95 6/9K sleeve, there was more extensive cracking at the base of the sleeve and some buckling and slumping of the sleeve (the height of the sleeve was reduced by up to 10 mm after moulding). The KALMINEX 2000XP flat topped dome shaped sleeve showed severe damage and the sleeve base was broken into several pieces. The KALMINEX 2000XP 6/9K sleeve was not tested.

In all instances, it was noticeable that after moulding, the first sidewall region of the collapsed feeder element was bent down past the horizontal i.e. was at an angle >90 to the bore axis.

COMPARATIVE EXAMPLE 2 Computer Simulation

A computer simulation (ABAQUS, manufactured by Abaqus Inc.) was conducted to evaluate the stresses imposed on a feeder system comprising a standard feeder sleeve with similar dimensions to a FEEDEX HD VSK sleeve and the feeder element 40 of FIG. 4. The advanced finite element analysis software includes a static and dynamic stress-strain resolver which was used for the simulations. The simulation was conducted by fixing the feeder element in the z-axis and then putting the model under a level of strain such that it compresses in the z-axis by a certain distance in a certain time. This puts various parts of the model under different stresses. The model was programmed with the mechanical properties of the sleeve and the feeder element, such that the stresses within the feeder sleeve can be simulated and the metal feeder element compresses.

Referring to FIG. 4, the feeder element 40 comprises a first end (base) 42 for mounting on a mould pattern; an opposite second end (top) 43 for receiving a feeder sleeve; and a bore 44 between the first and second ends 42, 43 defined by a stepped sidewall 45. The second end 43 is defined by a first sidewall region 46, said first sidewall region 46 being perpendicular to the bore axis A. A second sidewall region 47 is contiguous with the first sidewall region 46 and parallel to the bore axis A. The stepped sidewall 45 additionally comprises an alternating series of first 45 a and second 45 b sidewall regions. The second sidewall region 47 constitutes the first sidewall region of the second series 45 b. The first series of sidewall regions 45 a consists of two sidewall regions that are perpendicular to the bore axis A. The second series of sidewall regions 45 b consists of three sidewall regions that are parallel to the bore axis A.

FIG. 5 a shows part of the a feeder sleeve 50 mounted on the feeder element 40 of FIG. 4 before moulding. FIG. 5 b is an enlarged view of the base of the feeder element 50 mounted on feeder element 40 . . . FIG. 5 c shows an enlarged view of the same feeder sleeve 50 and feeder element 40 during moulding. The feeder sleeve cavity is indicated by arrow A. The shading, as shown in the key, represents the magnitude of the force imposed on the feeder sleeve 50. Referring to FIG. 5 c, it can be seen that the feeder element 40 deforms under pressure as expected. Surprisingly, its mounting surface 46 is forced incrementally downward at its peripheral edge. This leads to an uneven distribution of forces with a concentration on the inner wall of the feeder sleeve 50 (point loading) as indicated by arrow B.

EXAMPLE 1 Computer Simulation

The computer simulation of comparative example 2 suggests that the cracking observed in comparative example 1 may be caused by point loading on the inner wall of the feeder sleeve. The inventors attempted to alleviate this by changing the shape of the feeder element. The simulation was run again using the feeder element 52 of FIG. 6 in place of the feeder element 40 of FIG. 4. The inventive feeder element 52 is the same in all respects to that shown in FIG. 4 except that the mounting surface 54 of the feeder element 52 is inclined relative to the bore axis A at an angle of 60°. The base of the feeder sleeve 56 (FIG. 7 a) was profiled to the same angle.

FIGS. 7 a and 7 b show the feeder element 52 and the base of the corresponding feeder sleeve 56 before and during moulding respectively. FIG. 7 b shows that the force is no longer concentrated on the inner wall of the feeder sleeve 56 during moulding. It is more evenly distributed along the base of the feeder sleeve 56 so that no part of the base suffers from an excessive force. It will be noted that the area of maximum force (arrow B) is in a region of the sleeve remote from the feeder sleeve cavity (arrow A). Failure in this region will not cause fragments of feeder sleeve material to enter the casting and thereby cause defects.

EXAMPLE 1 Moulding Test

A feeder element 60 as shown in FIG. 8 was tested in combination with the flat topped dome shaped feeder sleeves listed in Table 2 below (as shown in FIG. 9):

TABLE 2 KALMINEX KALMINEX KALMINEX 2000ZP 95 2000XP Manufacturing Slurry formed Slurry formed Core shot Process Density (gcm⁻³) 0.55-0.65 0.85-0.95 0.55-0.65 Strength (kN)^(a) Low (4-5) Medium (10-11) Medium (1-12) ^(a)strength of standard cylindrical test body

The sleeve formulations vary according to the required product properties, however, all have the general formulation: 20-25% aluminium fuel; 10-20% oxidants and sensitisers; 5-10% organic binders; and 35-55% refractory fillers. The type of refractory fillers used has the most direct influence on both density and strength of the sleeves.

Referring to FIG. 8, the feeder element 60 is identical to the feeder element 20 shown in FIGS. 2 a and 2 b except that the first sidewall region 62 is inclined to the bore axis at an angle of 60°. The feeder element was manufactured from mild steel and has a thickness of 0.5 mm. The maximum diameter d is 92.9 mm and the height h is 35.4 mm. The diameter of the bore 26 at the base of the feeder element is 22.9 mm.

The feeder element 60 and feeder sleeve combinations were moulded as described above at various pressures between 420 PSI (2896 kPa) and 700 PSI (4826 kPa). The results are summarised in Table 3 below.

TABLE 3 KALMINEX KALMINEX KALMINEX Pressure 2000ZP 2000XP 95 420 PSI Sleeve buckled No failure No failure (2896 kPa) 460 PSI Sleeve buckled No failure No failure (3172 kPa) 520 PSI Sleeve buckled No failure No failure (3585 kPa) 580 PSI Sleeve buckled No failure No failure (3999 kPa) 600 PSI Sleeve buckled No failure No failure (4137 kPa) 700 PSI Sleeve buckled Cracked at dome No failure (4826 kPa) 700 PSI Collapsed Cracked at dome Buckled on (4826 kPa) one side of Repeat test sleeve

Feeder Element 60 and KALMINEX 2000ZP Feeder Sleeve

This combination was the weakest of those tested and showed signs of failure from low moulding pressure (420 PSI; 2896 kPa). The feeder element did not compress fully and the feeder sleeve buckled. Despite this, there were no signs of cracking or breaking of the base of the feeder sleeve adjacent to the feeder element.

Feeder Element 60 and KALMIEX 2000XP Feeder Sleeve

This combination was successful to moderately high pressure (700 PSI; 4826 kPa). The feeder sleeve eventually suffered from horizontal cracking along the dome portion of the sleeve. This was attributed to the sleeve composition (binder) and the influence of the sleeve shape and method of manufacture (core-shot). The failure was not immediately obvious, only being noticed when the sleeve was excavated from the sand mould after ram up. As expected, the level of compression of the feeder element increased with the moulding pressure until the feeder element was almost completely compressed. No sleeve debris was discovered inside the feeder sleeve therefore this mode of failure would not necessarily lead to debris falling into the casting and causing casting defects.

The flat topped dome shaped KALMINEX 2000XP feeder sleeve was employed with a conventional feeder element 20 in Comparative, Example 1 where it failed at much lower pressures. At just 380 PSI (2620 kPa), the feeder sleeve slumped and cracked along its base and at 620 PSI (4275 kPa) it suffered severe damage.

Feeder Element 60 and KALMIEX 95 Feeder Sleeve

This combination was also very successful. The feeder element 60 compressed and the first failure of the feeder sleeve occurred only at moderately high pressure (700 PSI; 4826 kPa). No feeder sleeve debris was discovered inside the feeder sleeve after it buckled therefore the failure would not necessarily have led to casting defects if the mould had been poured.

The KALMINEX 95 6/9K feeder sleeve was employed with a conventional feeder element 20 in Comparative Example 1 with very different results. The feeder sleeve suffered from cracking along its base at just 380 PSI (2620 kPa). At 620 PSI (4275 kPa) it suffered from more extensive cracking along its base and significant slumping. Cracking along the base is particularly problematic because chips of feeder sleeve may enter the casting.

It can be clearly seen that feeder element 60 of the present invention provides advantages over conventional feeder elements such as feeder element 20 shown in Comparative Example 1. When used in combination with feeder element 52 the medium strength feeder sleeves KALMINEX 2000XP and KALMINEX 95 are successful to much higher pressures. Further, when the feeder sleeves do eventually fail their mode of failure is less likely to lead to casting defects.

EXAMPLE 2 Compression Test

Referring to FIG. 10 a, force is plotted against plate displacement for a KALMINEX 2000ZP 6/9K feeder sleeve (as shown in FIG. 3 b) without a feeder element test piece. It will be noted that as force is increased, there is compression of the feeder sleeve associated with the natural flexibility (compressibility) of the feeder sleeve until a critical force is applied (point Z), referred to herein as the sleeve crush strength (approximately 4.5 kN) after which point the compression of the sleeve proceeds steadily under a reducing loading.

Referring to FIG. 10 c, force is plotted against plate displacement for a feeder element test piece 10 with α=80° and a KALMINEX 2000ZP 6/9K feeder sleeve, the base of which was profiled at an angle of 80°. It will be noted that as force is increased, there is minimal compression of the feeder element and sleeve, until a critical force is applied (point A), referred to herein as the initial feeder element crush strength, after which compression proceeds rapidly under a lower loading, with point B marking the minimum force measurement after the initial feeder element test piece crush strength occurs. Further compression occurs and the force increases to a maximum (maximum feeder element crush strength, point C). When the feeder element test piece has reached or is close to its maximum displacement (point D) the force increases rapidly until the sleeve body begins to fracture. Visual inspection of the sleeve shows that at point A there is some fracturing of the bottom corner (internal base and wall) of the feeder sleeve.

FIG. 10 b shows the plot of force against plate displacement for a feeder element test piece 10 with α=90° and a KALMINEX 2000ZP 6/9K feeder sleeve that had a flat base. This shows a similar but smoother curve compared to that in FIG. 10 c (α=80°) and the initial displacement occurs at a lower applied force and continues for a long period. This is due to the initial feeder element test piece crush strength being lower but also, more significantly, it is due to damage of the feeder sleeve at the base due to the applied force from the feeder element test piece (damaging) breaking the feeder sleeve such that the feeder element is pushed up into the feeder sleeve and causes the measured displacement.

FIGS. 10 d and 10 e show the plots of force against plate displacement for feeder element test pieces 10 with α=70° and α=60° respectively when tested together with KALMINEX 2000ZP 6/9K feeder sleeves, the bases of which were profiled at an angle of 70° and 60° respectively. Comparing these plots with FIG. 10 c (α=80°) it can be seen that the initial feeder element test piece crush strength (A) increases with decreasing α. It was also noted that the amount of visible damage to the base of the sleeve was significantly reduced and was minimal for α=70° with no fracture of the sleeve being visible.

FIGS. 10 f and 10 g show plots of force against plate displacement for feeder element test pieces with α=50° and α=40° respectively when tested together with KALMINEX 2000ZP 6/9K feeder sleeves, the bases of which were profiled at an angle of 50° and 40° respectively. For both of these, the initial feeder element test piece crush strength (point A) is comparable with the previously measured feeder sleeve crush strength (Z, approximately 4.5 kN). However for both, there is greater displacement at point A compared to the typical sleeve crush point (point Z) due to the collapsing of the feeder element. No damage to the base of the feeder sleeve caused by the feeder element test piece was observed.

FIGS. 10 h and 10 i show plots of force against plate displacement for feeder element test pieces 10 with α=30° and α=20° respectively when tested together with KALMINEX 2000ZP 6/9K feeder sleeves, the bases of which were profiled at an angle of 30° and 20° respectively. Comparing these plots with FIG. 10 g (α=40°) it can be seen that the initial feeder element crush strength (A) now decreases with decreasing α and the amount of displacement before the initial feeder element crush strength is increased. This is thought to be partly due to the distance traveled during the crushing of the feeder element test piece and partly due to a small amount of compression of the feeder sleeve into the feeder element test piece itself at the base of the feeder sleeve.

The ideal initial crush strength of the feeder element will be dependent upon the feeder sleeve (compression strength) and the moulding pressures employed. The initial feeder element crush strength should clearly be lower than the sleeve crush (compression) strength and ideally, the initial crush strength should be lower than 3000 N. If the initial crush strength is too high then moulding pressure may cause failure of the feeder sleeve before the feeder element has a chance to compress. The ideal maximum crush strength is very much dependent on the application for which the feeder element core is intended i.e. the moulding pressure employed and the sleeve composition (strength). If the maximum crush strength were too high for the moulding pressures employed, then there would be insufficient collapsing of the feeder element and subsequently insufficient sand compaction. In addition, it would limit the type (strength) of sleeves that could be successfully employed. 

1. A feeder element for use in metal casting, said feeder element comprising: (iv) a first end for mounting on a mould pattern; (v) an opposite second end for receiving a feeder sleeve; and (vi) a bore between the first and second ends defined by a stepped sidewall; said feeder element being compressible in use whereby to reduce the distance between the first and second ends, wherein the stepped sidewall has a first sidewall region defining the second end of the element and a mounting surface for a feeder sleeve in use, said first sidewall region being inclined to the bore axis by less than 90° and a second sidewall region contiguous with the first sidewall region, said second sidewall region being parallel to or inclined to the bore axis at a different angle to the first sidewall region whereby to define a step in the sidewall.
 2. The feeder element of claim 1 comprising additional sidewall regions, whereby multiple steps in the sidewall are defined.
 3. The feeder element of claim 2, wherein at least one of the additional sidewall regions is inclined at a greater angle to the axis than the first sidewall region.
 4. The feeder element of any preceding claim, wherein the first sidewall region is inclined to the bore axis at an angle of between 5° and 85°.
 5. The feeder element of any preceding claim, wherein the first sidewall is inclined to the bore axis at an angle of between 30° and 70°.
 6. The feeder element of any preceding claim, wherein the initial crush strength is no more than 5000 N.
 7. The feeder element of any preceding claim, wherein the initial crush strength is at least 250 N.
 8. The feeder element of any preceding claim, wherein said compression in use is non-reversible.
 9. The feeder element of any preceding claim, wherein the stepped sidewall of the feeder element comprises a first series of sidewall regions in the form of rings interconnected and integrally formed with a second series of sidewall regions.
 10. The feeder element of claim 9, which is defined by the first sidewall region and one each of the first and second series of sidewall regions.
 11. The feeder element of claim 9 or 10, wherein the thickness of the sidewall regions is 0.2 to 1.5 mm.
 12. The feeder element as claimed in any one of claims 9 to 11, wherein said rings are circular.
 13. The feeder element of any one of claims 9 to 12, wherein said rings are planar.
 14. The feeder element of any one of claims 9 to 13, wherein the sidewall regions are of substantially uniform thickness, so that the diameter of the bore of the feeder element increases from the first end to the second end of the feeder element.
 15. The feeder element of any one of claims 9 to 14, wherein the second series of sidewall regions are annular.
 16. The feeder element of any one of claims 9 to 15, wherein the first end of the feeder element is defined by a sidewall region having a greater length than the other sidewall regions of the corresponding series.
 17. The feeder element of any one of claims 9 to 16, wherein the sidewall region defining the first end of the feeder element is inclined to the bore axis by an angle of 5 to 30°.
 18. The feeder element of any one of claims 9 to 17, wherein the thickness of the sidewall regions is from 4 to 24% of the distance between the inner and outer diameters of the first sidewall region(s).
 19. The feeder element of claim 18, wherein a free edge of the sidewall region defining the first end of the feeder element has an inwardly directed annular flange or bead.
 20. A feeder system for metal casting comprising a feeder element in accordance with any one of claims 1 to 19 and a feeder sleeve secured thereto.
 21. A feeder system in accordance with claim 20, in which the feeder sleeve is secured to the feeder element by adhesive or by being a push fit with the feeder element or by moulding the sleeve around part of the feeder element.
 22. A feeder system in accordance with claim 20 or 21, wherein the base of the feeder sleeve is profiled at the same angle as the first sidewall region of the feeder element of any one of claims 1 to
 20. 23. A feeder system in accordance with any one of claims 20 to 22, wherein the sleeve strength is at least 5 kN and less than 20 kN. 